EEG_EM_New_Technique_TRANSVERSE_FLUX (TF) (Provisional Patent Applied for)

[solarlab]

Thanks Fella's for the contributions, really appreciate the input

For the Proof-of-Concept Prototype a known industry type electrical steel will be used
and the fabrication will be done by a professional lamination and annealing company.

Since this is new and novel concept, plus I plan on writing a paper on it; I think doing
it this way would be the best approach initially. Pretty expensive but considering the
ramifications (and pushback that I'm sure will ensue) the development, if successful,
will be much easier to defend.

There are many who believe Excess Energy can not exist and thus can not be achieved.
If they are proven wrong by this EE_TFG device then at least some of their arguments
will be closed off.

Should this device perform, as I believe it will, it also sets a baseline for all kinds of
future schemes - and many will be "dirt cheap" and "easy to do" just based on the
nature of the underlying science and technology involved.

Once I receive the Lamination Poles and determine the prototype material and
construction methods are viable then I'll look at "cost reduction" techniques. The
design and development cycle could be a few months - I'll update along the way.

But, for now, it's still just a novel theory; however it does pass the CAE Analysis and
does have a well founded basis in science (the 100 year old Lorentz Force Law), plus
there are similar proven devices already in use - however, they use rotating magnets, 
here we use electronically controlled electromagnets with no physical movement.

SL

[Ufopolitics]

Insulated (enameled) iron or steel wire is hard to find. Hobby Lobby has 24 gauge in 175 rolls for $2.99 used for making flower arrangements.
I wonder how this steel wire would work as the conductor. Would it improve the magnetic characteristics of the circuit enough to make up for the poor electrical conductivity of the steel such as higher voltage but lower current carrying ability ?

Hello ggx9,

This we are writing about it previously, is for the STEEL CORE, not for coil winding...So, it does not need to be insulated at all...

Ufopolitics

[ggx9]

Hello Ufopolitics.
To minimize eddy currents with methods such as thin steel sheets the sheets must be insulated from each other or the eddy currents will flow just as in solid steel.The insulation may be just a thin oxide but never the less there is insulation whether its visable thick vinyl or the invisible minimal oxide that forms from the heating of the steel sheet during manufacturing. The same will apply to any iron wire that is used as a core. 
I expect wire to be of less magnetic performance, presuming similar alloy, because wire is round and will have more air spaces in the build.

[Ufopolitics]

Hello Ufopolitics.
To minimize eddy currents with methods such as thin steel sheets the sheets must be insulated from each other or the eddy currents will flow just as in solid steel.The insulation may be just a thin oxide but never the less there is insulation whether its visable thick vinyl or the invisible minimal oxide that forms from the heating of the steel sheet during manufacturing. The same will apply to any iron wire that is used as a core.
I expect wire to be of less magnetic performance, presuming similar alloy, because wire is round and will have more air spaces in the build.

@ggx9,

Did you know that on the 19 Century, the Gramme Ring Armature Cores, on large Industrial Rating of High Amperage, High Voltage Dynamos, were made of fine steel wires?

And MIG Welder Iron wire, or a Steel Alloy, maybe used for this purposes...the air gaps between wires are negligible.

Ufopolitics

[Ufopolitics]

@solarlab :

I am sorry we have -all the sudden- hijacked your Thread...let me know and I will erase all our posts, that you do not want here.

I can just move this conversation somewhere else...but to me it is important, because some geometries will not allow for laminated steel sheets...

Regards friend.

Ufopolitics